T1 - Development of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) fibers for skin tissue engineering
T2 - Effects of topography, mechanical, and chemical stimuli
AU - Kuppan, Purushothaman
AU - Vasanthan, Kirthanashri S.
AU - Sundaramurthi, Dhakshinamoorthy
AU - Krishnan, Uma Maheswari
AU - Sethuraman, Swaminathan
PY - 2011/9/12
Y1 - 2011/9/12
N2 - Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV), a biodegradable polyester, was electrospun to form defect-free fibers with high surface-area-to-volume ratio for skin regeneration. Several parameters such as solvent ratio, polymer concentration, applied voltage, flow rate, and tip-to-target distance were optimized to achieve defect-free morphology. The average diameter of the PHBV fibers was 724 ± 91 nm. PHBV was also solvent-cast to form 2-D films, and its mechanical properties, porosity, and degradation rates were compared with PHBV fibers. Our results demonstrate that PHBV fibers exhibited higher porosity, increased ductility, and faster degradation rate when compared with PHBV 2-D films (p < 0.05). In vitro studies with PHBV fibers and 2-D films were carried out to evaluate the adhesion, viability, proliferation, and gene expression of human skin fibroblasts. Cells adhered and proliferated on both PHBV fibers and 2-D films. However, the proliferation of cells on the surface of PHBV fibers was comparable to tissue culture polystyrene (TCPS, control) (p > 0.05). The gene expression of collagen I and elastin was significantly up-regulated when compared with TCPS control, whereas collagen III was down-regulated on PHBV fibers and 2-D film after 14 days in culture. The less ductile PHBV 2-D films showed higher levels of elastin expression. Furthermore, the PHBV fibers in the presence and absence of an angiogenesis factor (R-Spondin 1) were evaluated for their wound healing capacity in a rat model. The wound contracture in R-Spondin-1-loaded PHBV fibers was found to be significantly higher when compared with PHBV fibers alone after 7 days (p < 0.05). Furthermore, the presence of fibers promoted an increase in collagen and aided re-epithelialization. Thus our results demonstrate that the topography and mechanical and chemical stimuli have a pronounced influence on the cell proliferation, gene expression, and wound healing.
AB - Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV), a biodegradable polyester, was electrospun to form defect-free fibers with high surface-area-to-volume ratio for skin regeneration. Several parameters such as solvent ratio, polymer concentration, applied voltage, flow rate, and tip-to-target distance were optimized to achieve defect-free morphology. The average diameter of the PHBV fibers was 724 ± 91 nm. PHBV was also solvent-cast to form 2-D films, and its mechanical properties, porosity, and degradation rates were compared with PHBV fibers. Our results demonstrate that PHBV fibers exhibited higher porosity, increased ductility, and faster degradation rate when compared with PHBV 2-D films (p < 0.05). In vitro studies with PHBV fibers and 2-D films were carried out to evaluate the adhesion, viability, proliferation, and gene expression of human skin fibroblasts. Cells adhered and proliferated on both PHBV fibers and 2-D films. However, the proliferation of cells on the surface of PHBV fibers was comparable to tissue culture polystyrene (TCPS, control) (p > 0.05). The gene expression of collagen I and elastin was significantly up-regulated when compared with TCPS control, whereas collagen III was down-regulated on PHBV fibers and 2-D film after 14 days in culture. The less ductile PHBV 2-D films showed higher levels of elastin expression. Furthermore, the PHBV fibers in the presence and absence of an angiogenesis factor (R-Spondin 1) were evaluated for their wound healing capacity in a rat model. The wound contracture in R-Spondin-1-loaded PHBV fibers was found to be significantly higher when compared with PHBV fibers alone after 7 days (p < 0.05). Furthermore, the presence of fibers promoted an increase in collagen and aided re-epithelialization. Thus our results demonstrate that the topography and mechanical and chemical stimuli have a pronounced influence on the cell proliferation, gene expression, and wound healing.
UR - https://www.scopus.com/pages/publications/80052768917
UR - https://www.scopus.com/inward/citedby.url?scp=80052768917&partnerID=8YFLogxK
U2 - 10.1021/bm200618w
DO - 10.1021/bm200618w
M3 - Article
C2 - 21800891
AN - SCOPUS:80052768917
SN - 1525-7797
VL - 12
SP - 3156
EP - 3165
JO - Biomacromolecules
JF - Biomacromolecules
IS - 9
ER -