T1 - Influence of 60Co gamma irradiation on the structural and optical properties of 2-aminopyridinium 4-nitrophenolate 4-nitrophenol crystals
AU - Thomas, Kezhia
AU - Parol, Vinay
AU - Karuppasamy, P.
AU - Pandian, Muthu Senthil
AU - Ramsamy, P.
AU - Prabhu, A. N.
N1 - Funding Information:
ANP and KT are grateful to Dr P. K. Das, IISc, Bangalore, for SHG measurement and Dr. Suresh Kulkarni, DAMP, Manipal for providing photoluminescence experimental facility. The crystal growth work was supported by the UGC-DAE, Mumbai under the project grant of UDCSR/MUM/AO/CRS-M-314/2020/812 and BRNS project (Ref. 34/14/06/2016-BRNS/34032).
Funding Information:
ANP and KT are grateful to Dr P. K. Das, IISc, Bangalore, for SHG measurement and Dr. Suresh Kulkarni, DAMP, Manipal for providing photoluminescence experimental facility. The crystal growth work was supported by the UGC- DAE , Mumbai under the project grant of UDCSR/MUM/AO/CRS-M-314/2020/812 and BRNS project (Ref. 34/14/06/2016-BRNS/34032 ).
Publisher Copyright:
© 2022 Korean Physical Society
PY - 2022/5
Y1 - 2022/5
N2 - In this article, effect of gamma irradiation on the structural and optical properties of 2-aminopyridinium 4-nitrophenolate 4-nitrophenol (2AP4N) has been reported. The grown crystals of 2AP4N were exposed to 60Co gamma rays with a dose of 50 kGy and 100 kGy. The radiation-induced effects were analyzed using X-ray diffraction, FT-IR, UV–visible, photoluminescence techniques. The refractive index was determined using a long arm spectrometer. The structural properties of the pristine and irradiated crystals were studied using powder XRD. The peak intensity decrease after irradiation may be attributed to the formation of point defects. The UV visible study reveals that the energy gap has decreased after irradiation and then has increased for the higher dose. The intensity variation in the PL spectra is due to colour center mechanism. The SHG efficiency of 2AP4N crystals was found to be unaffected by gamma irradiation.
AB - In this article, effect of gamma irradiation on the structural and optical properties of 2-aminopyridinium 4-nitrophenolate 4-nitrophenol (2AP4N) has been reported. The grown crystals of 2AP4N were exposed to 60Co gamma rays with a dose of 50 kGy and 100 kGy. The radiation-induced effects were analyzed using X-ray diffraction, FT-IR, UV–visible, photoluminescence techniques. The refractive index was determined using a long arm spectrometer. The structural properties of the pristine and irradiated crystals were studied using powder XRD. The peak intensity decrease after irradiation may be attributed to the formation of point defects. The UV visible study reveals that the energy gap has decreased after irradiation and then has increased for the higher dose. The intensity variation in the PL spectra is due to colour center mechanism. The SHG efficiency of 2AP4N crystals was found to be unaffected by gamma irradiation.
UR - http://www.scopus.com/inward/record.url?scp=85124473950&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=85124473950&partnerID=8YFLogxK
U2 - 10.1016/j.cap.2022.02.001
DO - 10.1016/j.cap.2022.02.001
M3 - Article
AN - SCOPUS:85124473950
SN - 1567-1739
VL - 37
SP - 1
EP - 7
JO - Current Applied Physics
JF - Current Applied Physics
ER -