T1 - Studies on LPG Sensing Property of Polyaniline / BaZrO3 Composites
AU - Khened, B. S.
AU - Machappa, T.
AU - Pradeep, M. V.N.
AU - Ambika Prasad, M. V.N.
AU - Sasikala, M.
PY - 2016/1/1
Y1 - 2016/1/1
N2 - Polyaniline (PANI) / Barium zirconate (BaZrO3) composites were prepared by insitu polymerization with 10, 20, 30, 40, 50 wt% of BaZrO3 in polyaniline and characterized by FTIR spectra, X-ray diffraction and scanning electron microscopy. Thermally activated behaviour was seen in D.C. conductivity measurements, where increase in conductivity with increase in temperature was observed. Maximum conductivity was seen in 40 wt% of BaZrO3 in polyaniline. A.C. conductivity studies reveal increase in conductivity of all the composites with increase in frequency. On exposure to LPG gas, variation in resistance of the composites was observed.
AB - Polyaniline (PANI) / Barium zirconate (BaZrO3) composites were prepared by insitu polymerization with 10, 20, 30, 40, 50 wt% of BaZrO3 in polyaniline and characterized by FTIR spectra, X-ray diffraction and scanning electron microscopy. Thermally activated behaviour was seen in D.C. conductivity measurements, where increase in conductivity with increase in temperature was observed. Maximum conductivity was seen in 40 wt% of BaZrO3 in polyaniline. A.C. conductivity studies reveal increase in conductivity of all the composites with increase in frequency. On exposure to LPG gas, variation in resistance of the composites was observed.
UR - http://www.scopus.com/inward/record.url?scp=84963533503&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=84963533503&partnerID=8YFLogxK
U2 - 10.1016/j.matpr.2016.01.022
DO - 10.1016/j.matpr.2016.01.022
M3 - Article
AN - SCOPUS:84963533503
SN - 2214-7853
VL - 3
SP - 369
EP - 375
JO - Materials Today: Proceedings
JF - Materials Today: Proceedings
IS - 2
ER -